China High Quality PFA Material Data Sheet Factory – DY-4020-01 Membrane Grade PVDF – DONGTAI
China High Quality PFA Material Data Sheet Factory – DY-4020-01 Membrane Grade PVDF – DONGTAI Detail:
Typital Properties
|
NO. |
NAME OF INDEX |
UNIT |
INDEX |
|
1 |
Appearance |
- |
White Powder |
|
2 |
Relative Density |
g/cm3 |
1.77-1.79 |
|
3 |
Melting Point |
℃ |
165-175 |
|
4 |
Melting flow index |
g/10min |
10-20（5kg） |
|
5 |
Tensile Strength |
MPa（23℃,≧） |
25 |
|
6 |
Percentage of breaking elongation |
%（23℃,≧） |
20 |
|
7 |
Shore hardness type D |
≧ |
70 |
|
8 |
Moisture Content |
% |
≤0.1 |
|
9 |
Thermal Decomposition Temperature |
℃ |
382-393 |
The index standard refers to T / FSI 027-2019, and the index data is only for customers’ reference.
Storage and Attention
The products mainly have three packaging forms: two-layer polyethylene plastic bag packaging, carton packaging and ton bag packaging for customers to choose. Daily storage in a clean and dry warehouse to prevent the introduction of impurities. This product is non-toxic and harmless at room temperature, but it should be noted that the processing temperature should not exceed 350 ℃, so as to prevent toxic gas from decomposition.
Product detail pictures:
Related Product Guide:
We strive for excellence, service the customers", hopes to become the best cooperation team and dominator enterprise for personnel, suppliers and customers, realizes value share and continuous promotion for China High Quality PFA Material Data Sheet Factory – DY-4020-01 Membrane Grade PVDF – DONGTAI , The product will supply to all over the world, such as: Lebanon, Barbados, Oman, Wide selection and fast delivery for you! Our philosophy: Good quality, great service, keep improving. We are looking forward that more and more oversea friends join in our family for further development near the future!
By Frances from Naples - 2017.12.09 14:01
Goods just received, we are very satisfied, a very good supplier, hope to make persistent efforts to do better.
By Roberta from Armenia - 2018.09.29 13:24